氟橡胶FKM
For more information, please send an email or call our hotline.
|
类别 |
通用 |
胶料类型 |
氟橡胶FKM |
||
|
配方编号 |
|
|
|
||
|
检测项目 |
|
||||
|
测试条件 |
常规物性 |
单位 |
FKM60 |
FKM70 |
FKM80 |
|
一段:170℃*10min |
硬度（Hardness） |
邵氏（A)度 |
60±5 |
70±5 |
80±5 |
|
拉伸强度(Tensile strength) |
Mpa |
≥10 |
≥10 |
≥10 |
|
|
扯断伸长率(Elongation at Break) |
% |
≥200 |
≥175 |
≥150 |
|
|
密度(Specific Gravity) |
g/cm3 |
1.89±0.03 |
1.98±0.03 |
2.05±0.03 |
|
|
175℃*10min |
T10 |
M.s |
1:30±0:15s |
1:15±0:15s |
1:15±0:15s |
|
T90 |
M.s |
4:00±0:25s |
3:20±0:25s |
4:30±0:25s |
|
|
热空气老化 |
|
|
|||
|
250℃*70H |
硬度变化(Change in hardness) |
邵氏（A)度 |
0-5 |
0-5 |
0-5 |
|
拉伸强度变化率(Change in Tensile strength) |
% |
±15% MAX |
±15% MAX |
±15% MAX |
|
|
扯断伸长率变化率(Change in Elongation at Break) |
% |
±15% MAX |
±15% MAX |
±15% MAX |
|
|
23℃*70h |
硬度变化max(Change in hardness) |
邵氏（A)度 |
±5 |
±5 |
±5 |
|
拉伸强度变化率(Change in Tensile strength) |
% |
±30% MAX |
±30% MAX |
±30% MAX |
|
|
扯断伸长率变化率(Change in Elongation at Break) |
% |
±30% MAX |
±30% MAX |
±30% MAX |
|
|
体积变化率(Change in volume) |
% |
10% MAX |
10% MAX |
10% MAX |
|
|
200℃*22h*25% |
压缩永久变形(Compression set) |
% |
30% MAX |
30% MAX |
30% MAX |
|
—40℃*3min |
低温脆性(low temperature brittleness) |
|
—20℃ |
—15℃ |
—15℃ |
|
建议工艺（实测模温）： |
|
一段工艺:温度170-185℃,硫化3-5分钟. |
|||
|
类别 |
通用标准化 油封 |
胶料类型 |
氟橡胶FKM |
|
|
配方编号 |
|
|
|
|
|
检测项目 |
|
|||
|
测试条件 |
常规物性 |
单位 |
FKM70 |
FKM80 |
|
一段:170℃*10min |
硬度（Hardness） |
邵氏（A)度 |
70±5 |
80±5 |
|
拉伸强度(Tensile strength) |
Mpa |
≥10 |
≥10 |
|
|
扯断伸长率(Elongation at Break) |
% |
≥175 |
≥150 |
|
|
密度(Specific Gravity) |
g/cm3 |
1.99±0.03 |
2.06±0.03 |
|
|
175℃*10min |
T10 |
M.s |
1:15±0:15s |
1:15±0:15s |
|
T90 |
M.s |
5:10±0:25s |
5:10±0:25s |
|
|
热空气老化 |
|
|
||
|
250℃*70H |
硬度变化(Change in hardness) |
邵氏（A)度 |
0-5 |
0-5 |
|
拉伸强度变化率(Change in Tensile strength) |
% |
±15% MAX |
±15% MAX |
|
|
扯断伸长率变化率(Change in Elongation at Break) |
% |
±15% MAX |
±15% MAX |
|
|
23℃*70h |
硬度变化max(Change in hardness) |
邵氏（A)度 |
±5 |
±5 |
|
拉伸强度变化率(Change in Tensile strength) |
% |
±30% MAX |
±30% MAX |
|
|
扯断伸长率变化率(Change in Elongation at Break) |
% |
±30% MAX |
±30% MAX |
|
|
体积变化率(Change in volume) |
% |
10% MAX |
10% MAX |
|
|
200℃*22h*25% |
压缩永久变形(Compression set) |
% |
30% MAX |
30% MAX |
|
—40℃*3min |
低温脆性(low temperature brittleness) |
|
—15℃ |
—15℃ |
|
建议工艺（实测模温）： |
|
一段工艺:温度170-185℃,硫化3-5分钟. |
||