减震垫类/缓冲垫类
For more information, please send an email or call our hotline.
|
类别 |
减震垫类/缓冲垫类 |
胶种类型 |
NR/NR+BR |
|||||
|
配方编号 |
|
|
|
|||||
|
检测项目 |
|
|||||||
|
A |
测试条件 |
常规物性 |
单位 |
测试方法 |
典型值 |
典型值 |
典型值 |
典型值 |
|
23±2°C |
硬度(Hardness) |
邵氏A(Shore A) |
GB/T531 |
45 |
55 |
65 |
75 |
|
|
拉伸强度(Tensile strength) |
兆帕(Mpa) |
GB/T528 |
16 |
17 |
17.5 |
19 |
||
|
扯断伸长率(Elongation at Break) |
% |
680 |
625 |
570 |
460 |
|||
|
M300%定伸应力(300%Modulus) |
兆帕(Mpa) |
5.8 |
6.6 |
8.5 |
10.7 |
|||
|
撕裂强度(Tear Strength) |
KN/M |
GB/T529 |
45 |
50 |
60 |
65 |
||
|
比重(Specific Gravity) |
g/cm3 |
GB/T533 |
1.12 |
1.14 |
1.18 |
1.21 |
||
|
B |
(70°Cx22H x25%) |
压缩永久变形（Compression set） |
% |
GB/T7759 |
20 |
18 |
18.6 |
19 |
|
C |
热空气老化(Heat aging resistance ) |
|
|
|
|
|
|
|
|
70°Cx22H |
硬度变化(Change in hardness) |
邵氏A(Shore A) |
GB/T3512 |
5 |
4 |
3 |
4 |
|
|
拉伸强度变化率 (Change in Tensile strength) |
% |
-11 |
-4 |
-6 |
-5 |
|||
|
扯断伸长率变化率 (Change in Elongation at Break) |
% |
-23 |
-16 |
-14 |
-12 |
|||
|
D |
(40°Cx72H x50PPHM x20%) |
耐臭氧性能(Ozone resistance) |
不龟裂 (NO Crack) |
GB/T7762 |
无龟裂 |
无龟裂 |
无龟裂 |
无龟裂 |
|
E |
|
阿克隆磨耗(Akron abrasion) 44N,250rpm,1000转 |
cm3 |
GB/T1689 |
0.3 |
0.25 |
0.2 |
0.2 |
|
F |
|
单体耐久性能（5Hz） |
万次 |
|
40 |
43 |
45 |
48 |
|
G |
(-40°Cx3MIN) |
耐低温脆性(low temperature brittleness) |
<-40°C |
GB/T1682 |
-50 |
-44 |
-40 |
-40 |
留言咨询